Order Products : sales@su-jiao.com
DOW™ LLDPE GRSN-9820 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6TIimx_DOW-LLDPE-GRSN-9820-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOW GRSN-9820 NT 7 Linear Low Density Polyethylene (LLDPE) Resin is produced using UNIPOL™ PE Process Technology and is supplied in granular form. This resin is specifically designed as a carrier resin for color concentrates and other masterbatch systems. The fine particle size reduces the need for grinding, and the high surface area of granular resin allows for more uniform dispersion of concentrate in the final product. GRSN-9820 NT 7 is compatible with polyethylene and polypropylene resins and can be used in a wide variety of fabrication processes. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 20.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 11.7 | MPa | ASTM D638 |
| Fracture | 7.58 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 60 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 386 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 168 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 42.8 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.9 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 123 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 108 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PP 2012/078 Blue | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| Nypol® PA A3 ST HS UV5 PRTA011 NR427 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Hax™ HFX 521 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Iupilon® EHR3200 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ VERTON™ RVL36SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ VERTON™ |