Order Products : sales@su-jiao.com
ELEVATE™ EB561
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6SWHR3_ELEVATEEB561.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Excellent sealability, excellent impact strength, good optics and enhanced stabilization Application/Uses
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.929 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.55 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 6.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm, blown film | 103 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, blown film | 110 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 24.1 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 25.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 380 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 550 | % | ASTM D882 |
| Dart Drop Impact (32 µm, Blown Film) | 480 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm, Blown Film) | 74 | ASTM D2457 | |
| Haze (31.8 µm, Blown Film) | 4.8 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.25 mils; blow up ratio 2.5:1, die gap 35 mils. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 199 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRYCITE™ 8202 | The Dow Chemical Company | PS Alloy | TRYCITE™ |
| Next Nylon 66 Prime Series PG33-01ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Daelim Po1y® LH5570 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Grilon® BG-35 S | EMS-GRIVORY | Nylon 6 | Grilon® |
| Polifil® PS RP-HIPS | The Plastics Group | PS (HIPS) | Polifil® PS |