Category: | PC , Polycarbonate |
Manufacturer: | West Michigan Compounding |
Trademark: | EnviroPC |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 6SRdR1_EnviroPC520G30.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
EnviroPC 520G30 is a polycarbonate (PC) product, which contains a 30% glass fiber reinforced material. It is available in North America. The main characteristics are: high rigidity. |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Appearance |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
Ash Content | 30 | % | ASTM D5630 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength | 124 | MPa | ASTM D638 |
Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
Flexural Modulus | 6890 | MPa | ASTM D790 |
Flexural Strength | 152 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact | 110 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 146 | °C | ASTM D648 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Maxxam™ PP5120 B4 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
TECAMID™ 66 | Ensinger Inc. | Nylon 66 | TECAMID™ |
HOPELEN H1500 | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
Hostalen ACP 6541A UV | LyondellBasell Industries | HDPE | Hostalen |
Lumid® HI2302A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |