LNP™ THERMOCOMP™ IF00C compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6SLU2f_LNP-THERMOCOMP-IF00C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP IF00C is a compound based on Nylon 6/12 resin containing 60% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound IF-100-12 Product reorder name: IF00C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.68 | g/cm³ | |
| -- | 1.67 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 21400 | MPa | ASTM D638 |
| -- | 20100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 207 | MPa | ASTM D638 |
| Break | 202 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.0 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 18500 | MPa | ASTM D790 |
| -- 5 | 18200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 306 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 311 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 7 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 8 | 640 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.0 | J | ASTM D3763 |
| -- | 3.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 215 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 214 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 205 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 198 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP CUV448 | Sasol Polymers | PP Impact Copolymer | Sasol Polymers PP |
| Tenite™ Propionate 360E2R30016 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| APEX® 92-G2370A-75 | Teknor Apex Company | PVC, Flexible | APEX® |
| InnoPlus LL7410A | PTT Global Chemical Public Company Limited | LLDPE | InnoPlus |
| SABIC® PPcompound 8650MB1 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |