Order Products : sales@su-jiao.com
Kingfa MAC-851
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6SEioW_Kingfa-MAC-851.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa MAC-851 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa MAC-851 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 60 | % | ASTM D638 |
| Flexural Modulus 3 | 2400 | MPa | ASTM D790 |
| Flexural Strength 4 | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -32°C, 3.20 mm | 400 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 123 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 220 - 245 | °C | |
| Middle Temperature | 220 - 250 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 265°CInjection Speed: 60 to 90% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene M20P100-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| SLOVAMID® 66 CF 30 TS | Plastcom | Nylon 66 | SLOVAMID® 66 |
| ExxonMobil™ LDPE LD 101BA Wire & Cable | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Estane® 5714 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| POLYFLON™ F-201 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |