NILAMID® XS3 GF55 TF10
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6RqhzW_NILAMIDXS3GF55TF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
SPECIALTY PARTIALLY AROMATIC POLYAMIDE BLEND
PARTIALLY AROMATIC PA, 55% GLASS FIBER REINFORCED, 10% PTFE LUBRICATED |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.73 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow : 23°C | 0.30 | -- | % | ISO 294-4 |
| Flow : 23°C | 0.070 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.50 | -- | % | ISO 62 |
| Saturated, 23°C | 3.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 19000 | 17500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 190 | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | 2.7 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 66 | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 12 | 13 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 235 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | HB | -- | UL 94 | |
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 2000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPS1001 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| NYCOA Polyamide 5000 HSL | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| Geon™ Vinyl Flexible A5DU0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| IROGRAN® A 92 E 4738 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| OP - PC - Lubricated 15 PTFE | Oxford Polymers | PC | OP - PC - Lubricated |