OMIKRON TM 91 is an homopolymer polypropylene filled with 40% of talc for injection moulding, high processability. It is available in black version. Coloured on demand. OMIKRON TM 91 is suitable for moulding of items requiring stiffness and dimensional stability well. It's normally used in automotive industry , for electrical parts and where high thermal properties and low shrinkage are demands |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 12 | % | ISO 527-2 |
| Flexural Modulus | 3800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.5 | kJ/m² | ISO 180 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging (150°C) | 6.3 | day | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 210 - 260 | °C | |
| Middle Temperature | 210 - 260 | °C | |
| Front Temperature | 210 - 260 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Pressure | 9.00 - 11.0 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.500 - 1.00 | MPa |
| Injection instructions |
|---|
| Post Pressure: 60 - 80 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 6298 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| BJB Polyurethane PC-10 | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Ferro PP TPP20AR14WH | Ferro Corporation | PP Copolymer | Ferro PP |
| Jiangsu Sinarise ZM928 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| LNP™ LUBRICOMP™ JFL36 compound | SABIC Innovative Plastics | PESU | LNP™ LUBRICOMP™ |