Generic PP Homopolymer - Talc
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6QKoPC_Generic-PP-Homopolymer---Talc.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Talc This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.03 - 1.26 | g/cm³ | ASTM D792 |
| 23°C | 0.969 - 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 4.9 - 21 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.95 - 20 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 2.20 - 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.55 - 1.7 | % | ASTM D955 |
| Transverse flow : 23°C | 1.1 - 1.8 | % | ASTM D955 |
| 23°C | 0.87 - 1.2 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.030 - 0.050 | % | ASTM D570 |
| 23°C, 24 hr | 0.020 - 0.052 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 84 - 106 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 72 - 79 | ASTM D2240 | |
| 23°C | 63 - 78 | ISO 868 | |
| Ball Indentation Hardness | 74.8 - 85.2 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1400 - 4700 | MPa | ASTM D638 |
| 23°C | 1980 - 4220 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 28.4 - 36.7 | MPa | ASTM D638 |
| Yield, 23°C | 27.9 - 35.2 | MPa | ISO 527-2 |
| Fracture, 23°C | 19.0 - 32.8 | MPa | ASTM D638 |
| Fracture, 23°C | 21.7 - 30.3 | MPa | ISO 527-2 |
| 23°C | 30.0 - 35.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.6 - 7.2 | % | ASTM D638 |
| Yield, 23°C | 1.7 - 8.4 | % | ISO 527-2 |
| Fracture, 23°C | 3.7 - 31 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 31 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1870 - 4330 | MPa | ASTM D790 |
| 23°C | 1840 - 4220 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 33.8 - 62.4 | MPa | ASTM D790 |
| 23°C | 44.8 - 50.6 | MPa | ISO 178 |
| Yield, 23°C | 51.4 - 55.6 | MPa | ASTM D790 |
| Fracture, 23°C | 44.8 - 59.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.3 - 4.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 10 - 40 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 20 - 39 | J/m | ASTM D256 |
| 23°C | 2.0 - 6.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 210 - 590 | J/m | ASTM D256 |
| 23°C | 8.5 - 9.5 | kJ/m² | ISO 180 |
| Dart Drop Impact (23°C) | 0.113 - 1.03 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 0.339 - 0.943 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 110 - 139 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 109 - 133 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 58.5 - 91.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 59.2 - 91.1 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 85.0 - 157 | °C | ASTM D1525 |
| -- | 88.3 - 158 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 165 - 182 | °C | |
| -- | 160 | °C | ISO 3146 |
| CLTE - Flow | |||
| -- | 6.0E-5 - 8.1E-5 | cm/cm/°C | ASTM D696 |
| -- | 6.0E-5 - 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 9.8E+15 - 1.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+13 - 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 596 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 642 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 550 - 806 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 | % | ASTM D2863 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | 46 - 47 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 - 110 | °C | |
| Drying Time | 1.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.070 - 0.20 | % | |
| Suggested Max Regrind | 16 | % | |
| Rear Temperature | 204 - 225 | °C | |
| Middle Temperature | 211 - 221 | °C | |
| Front Temperature | 190 - 247 | °C | |
| Nozzle Temperature | 188 - 239 | °C | |
| Processing (Melt) Temp | 198 - 248 | °C | |
| Mold Temperature | 30.0 - 66.1 | °C | |
| Injection Pressure | 5.86 - 105 | MPa | |
| Holding Pressure | 3.28 - 65.0 | MPa | |
| Back Pressure | 0.241 - 0.423 | MPa | |
| Screw Speed | 49 - 125 | rpm | |
| Clamp Tonnage | 3.4 - 4.5 | kN/cm² | |
| Cushion | 4.76 - 9.53 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - TalcThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PE LD2923B | Trademark Plastics Corporation | LDPE | Trademark PE |
| CompaDur® 121 GF 20 FR natural (012) | DimeLika Plast GmbH | PBT | CompaDur® |
| DOMAMID® 28 | DOMO Caproleuna GmbH | Nylon 6 | DOMAMID® |
| IDI BMC Rosite 3250C | IDI Composites International | TS, Unspecified | IDI BMC |
| Sylvin 9058-90UV Red 671 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |