ARLEN™ C240
| Category: | Nylon 6T , Polyamide 6T |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | ARLEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6POvyd_ARLEN-C240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ARLEN™C240 is a polyamide 6T (nylon 6T) material, which contains a 40% glass fiber reinforced material. This product is available in North America,. ARLEN™The main characteristics of C240 are: flame retardant/rated flame. ARLEN™Typical application areas of C240 are: electrical/electronic applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.53 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow : 2.00mm | 0.40 | -- | % | ASTM D955 |
| Transverse flow : 2.00mm | 0.80 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.20 | -- | % | ASTM D570 |
| 100°C, 24 hr | 2.8 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 210 | 180 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 3.0 | % | ASTM D638 |
| Flexural Modulus | 13000 | 9000 | MPa | ASTM D790 |
| Flexural Strength | 300 | 260 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 85 | 90 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | -- | °C | ASTM D648 |
| Glass Transition Temperature | 85.0 | -- | °C | DSC |
| Melting Temperature | 310 | -- | °C | |
| Linear thermal expansion coefficient | ASTM D696 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Lateral | 4.5E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | -- | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.50 | -- | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.018 | -- | ASTM D150 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Hopper Temperature | 50.0 - 90.0 | °C | |
| Rear Temperature | 300 - 325 | °C | |
| Middle Temperature | 315 - 335 | °C | |
| Front Temperature | 320 - 335 | °C | |
| Nozzle Temperature | 315 - 335 | °C | |
| Mold Temperature | 90.0 - 140 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 150 | rpm |
| Injection instructions |
|---|
| Injection Pressure: Medium Pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PE HD0390 | Qenos Pty Ltd | HDPE | Qenos PE |
| ADDILENE J 370 | ADDIPLAST | PP Copolymer | ADDILENE |
| Geon™ Vinyl Flexible R999A Black | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Eraclene® MS 80 U | Versalis S.p.A. | HDPE | Eraclene® |
| LNP™ THERMOCOMP™ LF002XXP-WT02005 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ THERMOCOMP™ |