LUVOCOM® TPE-7711/GY Datasheet,TPE,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®TPE-7711/GY is a thermoplastic elastomer (TPE) material, which contains carbon fiber reinforcement. This product is available in Europe,. LUVOCOM®The main features of TPE-7711/GY are: Conductivity Electrostatic protection Typical application areas include: engineering/industrial accessories Handle

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Features	Conductivity Electrostatic discharge protection
Uses	Handle Roller Bearing
Appearance	Grey

Physical	Nominal Value	Unit	Test Method
Density	1.04	g/cm³	ISO 1183
Molding Shrinkage	1.5 - 2.0	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.30	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	85		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	200	MPa	ISO 527-2
Tensile Stress (Break)	8.00	MPa	ISO 527-2
Tensile Strain (Yield)	500	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	33	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1fU

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	1.0E+2	ohms	IEC 60167

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	85.0	°C
Drying Time - Desiccant Dryer	2.0 - 3.0	hr
Suggested Max Moisture	0.010	%
Rear Temperature	160 - 185	°C
Middle Temperature	170 - 190	°C
Front Temperature	175 - 195	°C
Nozzle Temperature	180 - 200	°C
Processing (Melt) Temp	200	°C
Mold Temperature	25.0 - 55.0	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.01%, otherwise molecular degradation may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.01%, otherwise molecular degradation may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6ODxmR_LUVOCOM-TPE-7711-GY.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Wanthane® WHT-1690AB	Wanhua Chemical Group Co., Ltd.	TPU-Polyester	Wanthane®
BP Flex A 6410 BLK	Buckeye Polymers, Inc.	TPE	BP Flex
HIVOREX 6200B	Lotte Chemical Corporation	HDPE	HIVOREX
Sylvin 8773-60D Grey 9504	Sylvin Technologies Incorporated	PVC, Rigid	Sylvin
Sylvin 8940-90 BLACK	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin