LNP™ VERTON™ UV00AS compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6NMNIU_LNPVERTONUV00AScompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON UV00AS is a compound based on Polyphtalamide resin containing 50% Long Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* VERTON* Compound UF70010HS Product reorder name: UV00AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Flow | 0.10 - 0.20 | % | Internal method |
| Transverse flow | 0.20 - 0.30 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.42 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 254 | MPa | ISO 527-2/5 |
| Fracture | 254 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.3 | % | ISO 527-2/5 |
| Fracture | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16100 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 388 | MPa | ISO 178 |
| -- 4 | 364 | MPa | ISO 178 |
| Flexural Strain at Break 5 | 2.5 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 40 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 70 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 64.0mm span | 296 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 273 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 4.9E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 316 - 327 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 332 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSHINE PAS703 | Polyram Ram-On Industries | ASA | RAMSHINE |
| Zeoforte® ZSC3195CX | Zeon Corporation | NBR | Zeoforte® |
| ISOTHANE® 8102-B | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU, Unspecified | ISOTHANE® |
| Karina IVORY PVC COMPOUND 105850-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DX03550 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |