Amodel® AT-6115 HS Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Amodel AT- 6115 HS is a 15% glass fiber reinforced toughened grade polyphthalamide (PPA) resin with higher elongation than other 15% glass fiber reinforced grade AMODEL resin. Specially developed for car snap-on electronic connectors. Good fluidity and short molding cycle. -Black: AT-6115 HS BK 324 natural color: AT-6115 HS NT

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight
Additive	Impact modifier heat stabilizer Lubricant demoulding
Features	Impact modification Fast molding cycle High liquidity Thermal Stability Lubrication Good demoulding performance Extended tensile rate
Uses	Valve/valve components Industrial components Industrial application Machine/mechanical parts Metal substitution Connector Parts under the hood of a car Automotive Electronics Application in Automobile Field General Shell
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Water temperature mold injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.22	--	g/cm³	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	1.0	--	%	ASTM D955
Transverse flow	1.1	--	%	ASTM D955
Water Absorption (24 hr)	0.20	--	%	ASTM D570

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	5380	4200	MPa	ASTM D638
23°C	5200	--	MPa	ISO 527-2
100°C	3100	--	MPa	ISO 527-2
Tensile Stress
Fracture, 23°C	126	--	MPa	ISO 527-2
Fracture, 100°C	68.3	--	MPa	ISO 527-2
--	122	95.8	MPa	ASTM D638
Tensile Elongation
Fracture	3.4	5.3	%	ASTM D638
Fracture, 23°C	4.1	--	%	ISO 527-2
Fracture, 100°C	7.7	--	%	ISO 527-2
Flexural Modulus
--	4410	3450	MPa	ASTM D790
23°C	4270	--	MPa	ISO 178
100°C	2340	--	MPa	ISO 178
Flexural Strength
--	165	115	MPa	ASTM D790
23°C	170	--	MPa	ISO 178
100°C	66.9	--	MPa	ISO 178
Compressive Strength	100	--	MPa	ASTM D695
Shear Strength	56.5	44.1	MPa	ASTM D732

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	11	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	76	--	kJ/m²	ISO 179/1eU
Notched Izod Impact
--	91	80	J/m	ASTM D256
23°C	12	--	kJ/m²	ISO 180/1A
Unnotched Izod Impact
--	850	--	J/m	ASTM D256
23°C	55	--	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	298	--	°C	ISO 75-2/B
1.8 MPa, not annealed	251	--	°C	ISO 75-2/A
1.8 MPa, annealed	260	--	°C	ASTM D648
Melting Temperature	305	--	°C	ISO 11357-3, ASTM D3418
Linear thermal expansion coefficient				ASTM E831
Flow : 0 to 100°C	2.2E-5	--	cm/cm/°C	ASTM E831
Flow : 100 to 200°C	3.0E-5	--	cm/cm/°C	ASTM E831
Lateral : 0 to 100°C	9.0E-5	--	cm/cm/°C	ASTM E831
Lateral : 100 to 200°C	1.2E-4	--	cm/cm/°C	ASTM E831

Additional Information
调节后的 Conditioned to 50% RH in accordance with 1SO-1110, Accelerated Method.

Injection instructions
射出速度： 3〜4英寸/秒保压压力：射出压力的50%

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6MgnC2_Amodel-AT-6115-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
THERMOLAST® K TC6PAN (Series: AD/PA)	KRAIBURG TPE	TPE	THERMOLAST® K
Ebalta HFG / PUR 11	Ebalta Kunststoff GmbH	PUR, Unspecified	Ebalta
Ebalta AH 140 / TC 90-1	Ebalta Kunststoff GmbH	Epoxy	Ebalta
Hostalen PP H2483	LyondellBasell Industries	PP Copolymer	Hostalen PP
LUBAN™ 1101 RC	Oman Oil Refineries & Petroleum Indistries Co. (Orpic)	PP Homopolymer	LUBAN™