Triapol® Blends C3 K46 PRTA011 BS310 MSP
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Triapol® Blends |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6M1no3_Triapol-Blends-C3-K46-PRTA011-BS310-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polymer blend PC / ABS in color black, mainly characterized by its resistance to impact and temperature, have good dimensional stability and electrical insulation property. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 to 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 25 to 35 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 52.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 42 | % | |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GF 30 GID K1802 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Sindustris ABS LXR501 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Evermore PUR SC-636HR | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| ISOTHANE® 8101-B | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU, Unspecified | ISOTHANE® |
| Rigidex® HD5760UA | INEOS Olefins & Polymers Europe | HDPE Copolymer | Rigidex® |