INLUBE PA610GF30TF15
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INLUBE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6LGeWg_INLUBE-PA610GF30TF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Specific Volume | 0.690 | cm³/g | |
| Molding Shrinkage - Flow | 0.30 to 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.17 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 138 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 7930 | MPa | ASTM D790 |
| Flexural Strength | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| CLTE - Flow | 4.9E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 238 to 274 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS FS | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Europrene® 1789 | Versalis S.p.A. | SBR, Emulsion | Europrene® |
| Hostaform® C 9021 GV1/20 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| TechnoElast S A5002 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |
| TechnoMid PA6 S GF 15 GL | TechnoCompound GmbH | Nylon 6 | TechnoMid |