EMERGE™ PC/ABS 7570
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6L8ka1_EMERGE-PC-ABS-7570.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/ABS 7570 Advanced Resin is a high flow, ignition-resistant PC/ABS blend that contains no chlorinated or brominated additives. Its superior processing makes it ideal for injection molding of large, thin-wall, or intricate parts. EMERGE PC/ABS 7570 is suitable for use in a wide variety of applications in the Information Technology Equipment & Consumer Electronics industries. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183/B |
| Apparent Density | 0.67 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/3.8 kg | 20 | g/10 min | |
| 260°C/5.0 kg | 95 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm, Injection Molded) | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm, Injection Molded | 60.0 | MPa | |
| Break, 4.00 mm, Injection Molded | 47.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm, Injection Molded | 4.0 | % | |
| Break, 4.00 mm, Injection Molded | 40 | % | |
| Flexural Modulus 1(4.00 mm, Injection Molded) | 2700 | MPa | ISO 178 |
| Flexural Stress 2(4.00 mm, Injection Molded) | 92.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/A120 |
| -- | 98.0 | °C | ISO 306/B50 |
| Ball Indentation Temperature | 95.0 | °C | IEC 60335-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.60 mm, All Colors | V-0 | ||
| 2.50 mm, Natural plus Color Concentrate | V-0 | ||
| Glow Wire Flammability Index 4(2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature 5(2.00 mm) | 800 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® BMC 2800 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| MFE® -2 | Huachang Polymer Co., Ltd. | Vinyl Ester | MFE® |
| VITAMIDE® BF13BL6580 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| FHR Polypropylene AP5106-HA | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| MAJORIS DFR270 - 1298 | AD majoris | PP, Unspecified | MAJORIS |