Order Products : sales@su-jiao.com
DOW™ Butene 1220G1
| Category: | PE, Unspecified , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ Butene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6KLeM9_DOW-Butene-1220G1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Resistance | Internal method | ||
| 20 µm | 7.20 | J/cm³ | Internal method |
| 51 µm | 6.54 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 20 µm | 87.6 | J/cm³ | ASTM D882 |
| MD : 51 µm | 103 | J/cm³ | ASTM D882 |
| TD : 20 µm | 83.5 | J/cm³ | ASTM D882 |
| TD : 51 µm | 96.7 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 20 µm | 176 | MPa | ASTM D882 |
| 2% secant, MD : 51 µm | 167 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 207 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 207 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 10.1 | MPa | ASTM D882 |
| MD : Yield, 51 µm | 10.2 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 10.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 10.6 | MPa | ASTM D882 |
| MD : Break, 20 µm | 30.6 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 27.4 | MPa | ASTM D882 |
| TD : Break, 20 µm | 21.2 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 23.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 570 | % | ASTM D882 |
| MD : Fracture, 51 µm | 720 | % | ASTM D882 |
| TD : Break, 20 µm | 660 | % | ASTM D882 |
| TD : Fracture, 51 µm | 740 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709A | ||
| 20 µm | 76 | g | ASTM D1709A |
| 51 µm | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 20 µm | 91 | g | ASTM D1922 |
| MD : 51 µm | 110 | g | ASTM D1922 |
| TD : 20 µm | 310 | g | ASTM D1922 |
| TD : 51 µm | 220 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.7 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 116 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20°, 20.3 µm | 86 | ASTM D2457 | |
| 20°, 50.8 µm | 60 | ASTM D2457 | |
| Clarity | ASTM D1746 | ||
| 20.3 µm | 94.0 | ASTM D1746 | |
| 50.8 µm | 94.0 | ASTM D1746 | |
| Haze | ASTM D1003 | ||
| 20.3 µm | 7.4 | % | ASTM D1003 |
| 50.8 µm | 14 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 227 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 挤塑机：Gloucester 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：SFDM 模具间隙：70 密尔 (1.8 mm) 熔体温度：440°F (227°C) 输出：120 磅/小时 放大比：2.5:1 冷冻线高度：28 英寸 |
| Note Message | |
|---|---|
| 1 . | Modified rectangular measuring piece |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC C8065 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 152 HI HF | RTP Company | PP Copolymer | RTP |
| STERLENE™ CMV207E | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| Karina GRAY PVC COMPOUND 732D18/87-G-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPC TS4030 H | Polykemi AB | PP Copolymer | POLYfill |