Order Products : sales@su-jiao.com
SABIC® PPcompound G3230AE
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6IhG2m_SABIC-PPcompound-G3230AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound G3230AE is a 30% short glass fiber reinforced Polypropylene for unter-the-hood and structural applications. The base material is a PP homopolymer, optimized for low emission values. The glass fibres are chemically coupled to the PP matrix. This material has been designed to combine a good performance profile with fast processing. SABIC® PPcompound G3230AE is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.60 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 6500 | MPa | ISO 527-2/1A/5 |
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 97.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 3.7 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(Injection Molded) | 6300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 53 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C, Injection Molded) | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | °C | ISO 75-2/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 3.3E-5 | cm/cm/°C | |
| 23 to 80°C | 3.1E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 3-point loading |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® AX05 X03 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Vydyne® R413 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| EMOPLEN® A 1509 R G3 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| Polene EVA SV1055 | TPI Polene Public Company Limited | EVA | Polene EVA |
| Sylvin 9067-80 Grey 9469 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |