SABIC® PP PHC25
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6IUUHG_SABIC-PP-PHC25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade combines a very high impact strength, even at low temperatures, with a good stiffness. It has been designed for injection moulding applications requiring high impact resistance . It is also used as impact booster for compounds. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.6 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 | |
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1050 | MPa | ASTM D638 |
| -- | 1000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 21.0 | MPa | ASTM D638 |
| Yield | 22.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 10 | kJ/m² | |
| 0°C | 15 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C | 120 | J/m | ASTM D256A |
| 0°C | No Break | ASTM D256A, ISO 180/1A | |
| 23°C | No Break | ASTM D256A, ISO 180/1A | |
| -20°C | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 75.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 50.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 61.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 150 UV | RTP Company | PP, Unspecified | RTP |
| Tool-A-Thane UT-605 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| Chemlon® 60GSF6 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Sylvin 8365-70FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POROPHEN® GF 9202 L12 | SBHPP | Phenolic | POROPHEN® |