Boltaron 9816
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Boltaron Performance Products |
| Trademark: | Boltaron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6I0ssl_Boltaron-9816.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Boltaron 9816 is a clear blue tint proprietary rigid sheet developed specifically for aircraft interior applications that are required to meet the stringent FAA requirements for low heat release and smoke density as set forth in FAR 25.853 paragraphs (a) and (d). Boltaron 9816 offers excellent impact strength, abrasion resistance, stain and chemical resistance, and thermoformability. Gauges: .040 to .125 Standard Sizes: 50 x 99" Textures: Suede/Suede (SD/SD) Mirror/Mirror (MR/MR) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3310 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.8 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 to 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 74.4 | °C | |
| 1.8 MPa, Annealed | 80.6 | °C | |
| Vicat Softening Temperature | 95.5 | °C | ASTM D1525 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FAA Flammability 1 | 12.0 60.0 | sec | FAR 25.853 |
| Heat Release 2 | FAR 25.853 | ||
| 2 Min-Hrr | < 65 | ||
| Peak-Hrr | < 65 | kW/m² | |
| NBS Smoke Density | |||
| -- 3 | < 100 | ||
| -- 4 | < 200 | FAR 25.853 |
| Note Message | |
|---|---|
| 1 . | Pass |
| 2 . | A1 F, Part IV |
| 3 . | 1.5 Min, F814-84(b) |
| 4 . | 4 Min, F814-84(b) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T-27 MHS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Artenius AQUA | Artenius | PET | Artenius |
| DJSilicone NE-281 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Kepamid® 1330GFS | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| LNP™ THERMOCOMP™ DF008ERH compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |