Westlake LDPE EF412
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6HmAMr_Westlake-LDPE-EF412.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WESTLAKE polyethylene EF412 is a low-density polyethylene with very good optical and strength properties. This material is an excellent choice for bakery films and food packaging applications. Application/Uses General purpose clarity packaging Medium duty produce Bakery bags Bags for textile items |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 32 µm, blown film | 172 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, blown film | 200 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 24.1 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 18.6 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 350 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 700 | % | ASTM D882 |
| Dart Drop Impact 4(32 µm, Blown Film) | 100 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm, Blown Film) | 76 | ASTM D2457 | |
| Haze (31.8 µm, Blown Film) | 4.2 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.25 mils; blow up ratio 2.5:1, die gap 35 mils.Melt temperatures of 360° F - 390° F are recommended for Westlake Chemical EF412 with blow-up ratios of 1.5:1 or higher |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 199 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALGLASS H 07 H 20 G | RIALTI Srl | PP Homopolymer | RIALGLASS |
| Maxxam™ PD 20 TF Black | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Zythane® 6085AU | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| APEX® 1523E-8 | Teknor Apex Company | PVC, Flexible | APEX® |
| SQUARE® LSR1929-50AH/BH | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |