Vydyne® R530J NT0680
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6HH5o1_VydyneR530JNT0680.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vydyne R530J NT0680 is a natural, 30% glass-fiber-reinforced, PA66 resin that is heat-stabilized with an electrically neutral heat stabilizer. It is specially designed for electrical applications and devices requiring high dielectric strength, low conductivity, and corrosion resistance. R530J NT0680 is fully compliant with EU's Restriction of Hazardous Substances (RoHS) Directive 2011/65/EU. R530J NT0680 is certified by NSF (NSF-61), ACS (France), WRAS (UK) and KTW (Germany) for cold-water contact (23°C) with drinking water system components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Lateral flow : 23°C, 2.00mm | 0.90 | -- | % | ISO 294-4 |
| Traffic : 23°C, 2.00mm | 0.40 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 7400 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 195 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9600 | 6000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 270 | 190 | MPa | ISO 178 |
| Poisson's Ratio (23°C) | 0.40 | -- | ISO 527 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | 11 | kJ/m² | ISO 179 |
| 23°C | 11 | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 65 | 80 | kJ/m² | ISO 179 |
| 23°C | 75 | 85 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180 | |||
| -30°C | 10 | 11 | kJ/m² | ISO 180 |
| 23°C | 12 | 13 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00mm | 2.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C, 2.00mm | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.75 mm | HB | -- | UL 94 | |
| 1.5 mm | HB | -- | UL 94 | |
| 3.0 mm | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 - 310 | °C | |
| Middle Temperature | 280 - 310 | °C | |
| Front Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Processing (Melt) Temp | 285 - 305 | °C | |
| Mold Temperature | 65 - 95 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® L L2128 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Visiloy™ 2415T2U2 | Technical Polymers, LLC | ASA+PC | Visiloy™ |
| NuSil CV3-2289-1 | NuSil Technology | Silicone | NuSil |
| Adell Polyamide AT-33 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| GETILAN GPE/200 E | Crosspolimeri S.p.A. | XLPE | GETILAN |