INNOPOL® PP CS 1-2130
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6FxQ0B_INNOPOL-PP-CS-1-2130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-2130 is a 30 % talc-filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 1-2130 is recommended especially for producing parts, where high stiffness, low shrinkage, good heat-stability and excellent processability are required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.6 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 22 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 124 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 153 | °C | ISO 306/A120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Processing (Melt) Temp | 230 - 240 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Hold pressure: 30 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GFT15N050-N2 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Elastane™ 4760-92A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Hypro® PP-HP 35NS | Entec Polymers | PP Homopolymer | Hypro® |
| InnoPlus HD3355F | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| Sylvin 4260-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |