PENTESTER ET GV20 L H RC schwarz
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTESTER ET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6FoTQX_PENTESTER-ET-GV20-L-H-RC-schwarz.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyester PET, 20% glass fiber reinforced, impact modified, Recompound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 25 | kJ/m² | ISO 179/1eU |
| 23°C | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 180 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 245 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Additional Information |
|---|
| ISO Description: PET, MPRMC, 13-090; GF20The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.016 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 260 - 285 | °C | |
| Middle Temperature | 275 - 290 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 130 | °C | |
| Injection Pressure | 72.0 | MPa | |
| Holding Pressure | 36.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S BMX200K 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Sipolprene® 46185 | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Cogegum® AFR/760 | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| Lupoy® NF1005F 03R | LG Chem Ltd. | PC | Lupoy® |
| Petra® 130 BK-112 | BASF Corporation | PET | Petra® |