MAJORIS FT108 - 3182
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ErQNq_MAJORIS-FT108---3182.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FT108 - 3182 is a mineral filled polypropylene compound intended for injection moulding. The product is available in black (FT108 - 8229) and natural (FT108) but other colours can be provided on request. FT108 - 3182 has a easy flow very good processability, excellent surface quality. APPLICATIONS FT108 - 3182 is intended for components, which require good surface quality, good impact.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.2 - 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 6.0 | % | ISO 527-2/5 |
| Fracture | 26 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 119 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 64.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A |
| -- | 97.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® UT250 HR | Covestro - Polycarbonates | PC+PET | Makroblend® |
| SCHULABLEND® (PC/ABS) M/MB 5 | A. Schulman Europe | PC+ABS | SCHULABLEND® |
| Silopren® LSR 4060 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Telcar® TL EF-6109 | Teknor Apex Company | TPE | Telcar® |
| Karina IVORY PVC COMPOUND IRDB 40-LF-BR(CABELAUTO) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |