YUCLAIR® JH910
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SK Global Chemical |
| Trademark: | YUCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6EGmxU_YUCLAIR-JH910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
YUCLAIR JH910/JH910U are high density polyethylene resins with narrow molecular weight distribution. They offer high stiffness and impact resistance combined with good processability and low warpage. These resins are particularly suitable for the production of tote boxes, pails and crates. JH910U contains UV-stabilizer, for use in products requiring out-door weathering resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.5 | MPa | |
| Break | 9.81 | MPa | |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO S1803 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Axiall PVC 1802 Clear 7070 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| GAPEX® APP25GL01BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| LubriOne™ PC-20GF/15T | PolyOne Corporation | PC | LubriOne™ |
| Thermec N™ 4340R60H | Technical Polymers, LLC | PPA | Thermec N™ |