LEMALLOY® BX503A-1
| Category: | PPE+Nylon 6 , Polyphenylene Ether + Nylon 6 |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | LEMALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6DoyX5_LEMALLOY-BX503A-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEMALLOY® BX503A-1 is a Polyphenylene Ether + Nylon 6 (PPE+Nylon 6) material filled with filler. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of LEMALLOY® BX503A-1: Rigid. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.19 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 35.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow : 3.20 mm | 0.90 to 1.1 | -- | % | |
| Flow : 3.20 mm | 1.0 to 1.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 67.0 | 46.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.5 | 9.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 29 | 60 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3400 | 1800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 110 | 68.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 14 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | -- | °C | ISO 75-2/A |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 250 to 290 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Nozzle Temperature | 260 to 300 | °C | |
| Mold Temperature | 70.0 to 110 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1400 N | RTP Company | PESU | RTP |
| Ranger PBT PBT-403-M-G30 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Geon™ CPVC EC920 | PolyOne Corporation | CPVC | Geon™ CPVC |
| Hapcast™ 3736 | Hapco Inc. | TP, Unspecified | Hapcast™ |
| POLYFLAM® RPP 60335 CS1 5V | A. Schulman Europe | PP Homopolymer | POLYFLAM® |