LUVOCOM® 7-0755 Datasheet,Nylon 610,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®7-0755 is a polyamide 610 (nylon 6/10) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 7-0755 are: High stiffness high strength Good dimensional stability moisture resistance Wear-resistant Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry business/office supplies Handle

General Information
Filler / Reinforcement	Glass fiber reinforced material
Additive	PTFE lubricant
Features	Good dimensional stability Low friction coefficient Rigidity, high High strength Good wear resistance Lubrication Low or no water absorption
Uses	Handle Textile applications Engineering accessories Machine/mechanical parts Application in Automobile Field Business equipment Bearing
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.41	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.15	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	11000	MPa	ISO 527-2
Tensile Stress (Break)	200	MPa	ISO 527-2
Tensile Strain (Yield)	3.5	%	ISO 527-2
Flexural Modulus	9000	MPa	ISO 178
Flexural Stress	290	MPa	ISO 178
Coefficient of Friction
Dynamic	0.35
Static	0.25
Flexural Strain at Flexural Strength	4.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	140	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength
-30°C	85	kJ/m²	ISO 179/1fU
23°C	100	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	210	°C	ISO 75-2/A
Continuous Use Temperature	90.0	°C	UL 746B
CLTE - Flow	4.0E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.30	W/m/K	DIN 52612

Injection	Nominal Value	Unit
Drying Temperature
A	75.0	°C
B	105	°C
Drying time- A	6.0 - 10	hr
Suggested Max Moisture	0.10	%
Rear Temperature	240 - 270	°C
Middle Temperature	260 - 280	°C
Front Temperature	270 - 290	°C
Nozzle Temperature	270 - 290	°C
Processing (Melt) Temp	265	°C
Mold Temperature	70.0 - 100	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 610 , Polyamide 610
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6DXOeA_LUVOCOM-7-0755.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Modified Plastics MN6-FG10 SE BK	Modified Plastics, Inc.	Nylon 6	Modified Plastics
TIPPLEN® R 959 A	MOL Petrochemicals Co. Ltd.	PP Random Copolymer	TIPPLEN®
EnCom POM 0614 TF	EnCom, Inc.	Acetal (POM) Homopolymer	EnCom
KumhoSunny PC HCG2520FR	Shanghai KumhoSunny Plastics Co., Ltd.	PC	KumhoSunny PC
Capilene® W 50 V LE	Carmel Olefins Ltd.	PP Homopolymer	Capilene®