Order Products : sales@su-jiao.com
TRANSMARE® BIO 35LANF30-0.101
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® BIO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6DUPaL_TRANSMARE-BIO-35LANF30-0-101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® BIO-35LANF30-0.101 is a 30% BF-K100 bamboo fiber reinforced PLA based biopolymer. It combines a very high stiffness with good flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 84 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 5250 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 1.5 | % | ISO 527-2/50 |
| Flexural Modulus (Injection Molded) | 4750 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | < 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C, injection molding | 1.4 | kJ/m² | ISO 179/1A |
| 23°C, injection molding | 1.4 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C, injection molding | 7.8 | kJ/m² | ISO 179/1U |
| 23°C, injection molding | 7.3 | kJ/m² | ISO 179/1U |
| Notched Izod Impact | ISO 180/1A | ||
| -40°C, injection molding | 2.0 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 1.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C, injection molding | 8.5 | kJ/m² | ISO 180/1U |
| 23°C, injection molding | 7.3 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 52.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 67.0 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 | °C | |
| Middle Temperature | 175 | °C | |
| Front Temperature | 185 | °C | |
| Nozzle Temperature | 190 | °C | |
| Mold Temperature | 25.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| In specific cases pre-drying of this material might be required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylite® Profile™ 33541-00 | Reichhold Chemicals, Inc. | Polyester, TS | Polylite® Profile™ |
| TECHNO ABS R5601A | Techno Polymer America, Inc. | PC+ABS | TECHNO ABS |
| Sylvin 5132-75UV Clear Green 3182 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Yanshan PE 1600J | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| GLS PP YN06 HF | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |