RTP 2100 GB 20
| Category: | PEI , Polyether Imide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6Cf2Ps_RTP-2100-GB-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- RTP 2100 GB 20 is PEI, containing 20% glass beads, designed to provide low warpage. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 343 to 399 | °C | |
| Middle Temperature | 343 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Mold Temperature | 93.3 to 177 | °C | |
| Injection Pressure | 82.7 to 124 | MPa | |
| Back Pressure | 0.345 to 0.517 | MPa | |
| Clamp Tonnage | 6.9 to 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang C-8207N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| Vi-Chem PVC V148-85 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Eastar™ A150 | Eastman Chemical Company | Copolyester | Eastar™ |
| LARIPUR® LPR 6520 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| Sylvin 7833-80C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |