DINALON® B1S25 HI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupo Repol |
| Trademark: | DINALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6CCZvI_DINALON-B1S25-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DINALON® B1S25 HI is a Polyamide 6 (Nylon 6) product. It is available in Europe. Primary characteristic: impact resistant. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183/A |
| Humidity 1 | < 0.25 | % | ISO 15512/B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 25 | % | |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Flexural Stress | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 60 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | °C | ISO 306/B |
| Note Message | |
|---|---|
| 1 . | Karl-Fischer |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 3486/50 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Gallonprene® GP210-7002L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| FRIANYL® B3 V2 | Nilit Plastics | Nylon 6 | FRIANYL® |
| EcoLon® GF3060-BK1 | Wellman Engineering Resins | Nylon, Unspecified | EcoLon® |
| Karina IVORY PVC COMPOUND 75930-35/ 1-F-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |