VECTRA® A530

Category:	LCP , Liquid Crystal Polymer
Manufacturer:	Celanese Corporation
Trademark:	VECTRA®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6BwBeg_VECTRA-A530.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Best overall surface appearance with properties similar to A130. Less abrasive than glass fiber reinforced grades. Improved toughness over A130. Outstanding hydrolytic stability. Recommended where aesthetics are key. 30% mineral filled.

Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
FDA compliant
UL-Listing V-0 in natural and black at 0.38mm thickness per UL 94 flame testing, and UL-5VA in natural at 3.0mm. Relative-Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C.
UL = Underwriters Laboratories (USA)

General Information
Filler / Reinforcement	Mineral filler, 30% filler by weight
Features	Hydrolysis resistance Good toughness Halogen-free Excellent appearance Flame retardancy
Agency Ratings	EU 2002/96/EC (WEEE) FDA not rated
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1)
Resin ID (ISO 1043)	LCP

Physical	Nominal Value	Unit	Test Method
Density
--	1.65	g/cm³	ISO 1183
--	1650	kg/m³	ISO 1183 ¹
Molding Shrinkage
Vertical flow direction	0.70	%	ISO 294-4
Flow direction	0.20	%	ISO 294-4
Flow	0.20	%	ISO 2577 ²
Transverse flow	0.70	%	ISO 2577 ³

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	67		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	11000	MPa	ISO 527-2/1A/1
Tensile Stress (Break)	160	MPa	ISO 527-2/1A/5
Tensile Strain (Break)	4.6	%	ISO 527-2/1A/5
Flexural Modulus (23°C)	11900	MPa	ISO 178
Flexural Stress (23°C)	180	MPa	ISO 178
Compressive Modulus	9500	MPa	ISO 604
Compressive Stress (1% Strain)	60.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength
23°C	25	kJ/m²	ISO 179/1eA
23°C	25.0	kJ/m²	ISO 179/1eA ⁴
Charpy Unnotched Impact Strength
23°C	50	kJ/m²	ISO 179/1eU
23°C	50.0	kJ/m²	ISO 179/1eU ⁵
Notched Izod Impact (23°C)	27	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength (23°C)	40	kJ/m²	ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	203	°C	ISO 75-2/B
0.45 MPa	203	°C	ISO 75-2 ⁶
1.8 MPa, not annealed	190	°C	ISO 75-2/A
1.8 MPa	190	°C	ISO 75-2 ⁷
8.0 MPa, not annealed	121	°C	ISO 75-2/C
8.0 MPa	121	°C	ISO 75-2 ⁸
Vicat Softening Temperature
--	151	°C	ISO 306/B50
50°C/h, B (50N)	151	°C	ISO 306 ⁹
Melting Temperature
-- ¹⁰	280	°C	ISO 11357-3
-- ¹¹	280	°C	ISO 11357-3 ¹²
Linear thermal expansion coefficient			ISO 11359-2
Flow	1.0E-5	cm/cm/°C	ISO 11359-2
Lateral	3.0E-5	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity
--	1.0E+14	ohms·cm	IEC 60093
--	1.0E+12	ohms·m	IEC 60093 ¹³
Dielectric Strength	44	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	3.80		IEC 60250
1 MHz	3.20		IEC 60250
Dissipation Factor			IEC 60250
100 Hz	0.010		IEC 60250
1 MHz	0.016		IEC 60250
Arc Resistance	180	sec	Internal method
Comparative Tracking Index
--	200	V	IEC 60112
--	200		IEC 60112 ¹⁴

Flammability	Nominal Value	Unit	Test Method
Flame Rating	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature	150	°C
Drying Time	4.0 - 6.0	hr
Suggested Max Moisture	0.010	%
Hopper Temperature	20.0 - 30.0	°C
Rear Temperature	270 - 280	°C
Middle Temperature	275 - 285	°C
Front Temperature	280 - 290	°C
Nozzle Temperature	290 - 300	°C
Processing (Melt) Temp	285 - 295	°C
Mold Temperature	80.0 - 120	°C
Injection Pressure	50.0 - 150	MPa
Injection Rate	Fast
Holding Pressure	50.0 - 150	MPa
Back Pressure	0.00 - 3.00	MPa

Injection instructions
Manifold Temperature: 285 to 295°CZone 4 Temperature: 285 to 295°CFeed Temperature: 60 to 80°C

Note Message
1 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
2 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
3 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
4 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
5 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
6 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
7 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
8 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
9 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
10 .	10°C/min
11 .	10 °C/min
12 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
13 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
14 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???

Resin Grade	Manufacturer	Category	Trademark
SCHULAMID® 612 FS 4004	A. Schulman Europe	Nylon 612	SCHULAMID®
Badamid® LA70 GF50 MoS2 1%	Bada AG	Nylon 66	Badamid®
Arnite® TV4 270	DSM Engineering Plastics	PBT	Arnite®
DIGITALWAX® RD 095	DWS Systems	Unspecified	DIGITALWAX®
Hapflex™ 540	Hapco Inc.	TP, Unspecified	Hapflex™