NANCAR® 2865
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6Bfpqg_NANCAR-2865.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 2865 is a medium acrylonitrile butadiene copolymer with medium oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has superior processing characteristics, fast curing rate, low mold fouling and superior resilience properties. NANCAR® 2865 is recommended for use in applications requiring improved low temperature properties. It provides excellent extrusions and general processing improvement. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | |
| Mooney Viscosity (ML 1+4, 100°C) | 65 | MU | ASTM D1646 |
| Acrylonitrile Content - Bound | 28.0 | % | Internal Method |
| Solubility - in MEK | 100 | % | |
| Stabilizer | Non-staining |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.20 | % | ASTM D5688 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A 1 | 73 | ASTM D2240 | |
| Shore A 2 | 72 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 300% Strain 3 | 9.71 | MPa | |
| 300% Strain 4 | 10.5 | MPa | |
| 300% Strain 5 | 11.0 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Yield 6 | 28.2 | MPa | |
| Yield 7 | 27.8 | MPa | |
| Yield 8 | 28.6 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Break 9 | 610 | % | |
| Break 10 | 580 | % | |
| Break 11 | 560 | % | |
| Tear Strength | 59.8 | kN/m | ASTM D624 |
| Compression Set 12(100°C, 70 hr) | 60 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 13(100°C, 70 hr) | -6.0 | % | ASTM D865 |
| Change in Ultimate Elongation in Air 14(100°C, 70 hr) | -24 | % | ASTM D865 |
| Change in Durometer Hardness in Air 15(Shore A, 100°C, 70 hr) | 2.0 | ASTM D865 | |
| Change in Tensile Strength 16 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -7.0 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -26 | % | |
| Change in Ultimate Elongation 17 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -19 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -22 | % | |
| Change in Durometer Hardness 18 | ASTM D471 | ||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | -1.0 | ||
| Shore A, 100°C, 70 hr, in ASTM #3 Oil | -12 | ||
| Change in Volume 19 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM Oil #1 | 2.0 | % | |
| 100°C, 70 hr, in ASTM Oil #3 | 22 | % |
| Note Message | |
|---|---|
| 1 . | Cured for 60.0 min at 150°C |
| 2 . | Cured for 20.0 min at 150°C |
| 3 . | Cured for 20.0 min at 150°C |
| 4 . | Cured for 40.0 min at 150°C |
| 5 . | Cured for 60.0 min at 150°C |
| 6 . | Cured for 60.0 min at 150°C |
| 7 . | Cured for 40.0 min at 150°C |
| 8 . | Cured for 20.0 min at 150°C |
| 9 . | Cured for 20.0 min at 150°C |
| 10 . | Cured for 40.0 min at 150°C |
| 11 . | Cured for 60.0 min at 150°C |
| 12 . | Cured for 60.0 min at 150°C |
| 13 . | Cured for 40.0 min at 150°C |
| 14 . | Cured for 40.0 min at 150°C |
| 15 . | Cured for 40.0 min at 150°C |
| 16 . | Cured for 40.0 min at 150°C |
| 17 . | Cured for 40.0 min at 150°C |
| 18 . | Cured for 40.0 min at 150°C |
| 19 . | Cured for 40.0 min at 150°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SI-LINK™ AC DFDA-5488 NT | The Dow Chemical Company | PE, Unspecified | SI-LINK™ |
| Cheng Yu N6G35 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| Chemical Resources SAN900 | Chemical Resources, Inc. | SAN | Chemical Resources |
| Karina CLEAR PVC COMPOUND E-85/269-K-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-LOY™ AF3009 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |