DIC.PPS CZ-1030
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6BBZ9C_DIC-PPS-CZ-1030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.25 | % | |
| Across Flow | 1.1 | % | |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 100 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638 |
| Tensile Strength | 115 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 9000 | MPa | ASTM D790 |
| Flexural Strength | 170 | MPa | ASTM D790 |
| Compressive Strength | 130 | MPa | ASTM D695 |
| Poisson's Ratio | 0.36 | ||
| Coefficient of Friction 1 | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.20 | ||
| vs. Steel - Static | 0.20 | ||
| Flexural Elongation at Break | 1.2 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Unnotched Izod Impact | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 90°C | 2.0E-5 | cm/cm/°C | |
| Transverse : -30 to 90°C | 2.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+7 to 1.0E+8 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 to 340 | °C | |
| Middle Temperature | 300 to 340 | °C | |
| Front Temperature | 300 to 340 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | P=150KPa, V=0.3m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® K190-BPT-15 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Trexprene® A70CI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Bergamid™ A70 UF Grey VN-3921 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Escorene™ Ultra FL 00018 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Moplen EP548S | LyondellBasell Industries | PP Impact Copolymer | Moplen |