LNP LUBRICOMP RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Also known as: LNP* LUBRICOMP* Compound PDXR85514 Product reorder name: RX85514 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 1.2 - 1.4 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3800 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 43.0 | MPa | ISO 527-2/5 |
| Fracture | 71.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.3 | % | ISO 527-2/5 |
| Fracture | 5.3 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 3300 | MPa | ISO 178 |
| Flexural Stress | 106 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 241 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 97.0 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Ject® 1100V-20 | Premix, Inc. | TS, Unspecified | Premi-Ject® |
| Utomer UT880 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| 3M™ Dyneon™ Fluoroplastic THV 815GZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| Bynel® 22E804 | DuPont Packaging & Industrial Polymers | EA | Bynel® |
| Celanex® 2300 GV3/30 | Celanese Corporation | PBT | Celanex® |