LNP™ LUBRICOMP™ KG002 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 69Wdg1_LNP-LUBRICOMP-KG002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KG002 is a compound based on Acetal Copolymer resin containing 10% Graphite. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KL-4320 Product reorder name: KG002 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 2.3 | % | |
| Across Flow : 24 hr | 2.2 | % | |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3180 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 51.7 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2 |
| Break | 49.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.9 | % | ASTM D638 |
| Yield | 7.5 | % | ISO 527-2 |
| Break | 20 | % | ASTM D638 |
| Break | 19 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.56 | ||
| vs. Itself - Static | 0.44 | ||
| Wear Factor - Washer | 103 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 5.3 | J/m | ASTM D256 |
| 23°C 2 | 47 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D4812 |
| 23°C 3 | 690 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.50 | J | ASTM D3763 |
| -- | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 157 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 110 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 65.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 9.6E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT2500-01A | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Wellamid® MR409 22H-GY1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Nycal™ 2180N13H | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Keyflex® TO 1075AR | LG Chem Ltd. | TPC-ET | Keyflex® TO |
| NILAMID® XS3 GF40 | Nilit Plastics | Nylon, Unspecified | NILAMID® |