ENGAGE™ 7277
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 67ugR4_ENGAGE-7277.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™7277 is a kind of general purpose copolymer, which has good balance in cost/performance and is applied to polymer modification. Main features:
Application field:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.880 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 24 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, molded | 80 | ASTM D2240 | |
| Shore D, 1 second, molded | 26 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 3.70 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 13.9 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 720 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : Molding | 22.5 | MPa | ASTM D790 |
| 2% secant : Molding | 21.7 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 53.2 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -44.0 | °C | Internal method |
| Vicat Softening Temperature | 50.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 64.0 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 50.0 | °C | Internal method |
| Additional Information |
|---|
| 对无滑石粉产品测量的属性。 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | C mould |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 D | RTP Company | Nylon 612 | RTP |
| RTP 885 | RTP Company | Acetal (POM) Copolymer | RTP |
| Starflam AFR450B | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| LNP™ THERMOCOMP™ DF004XXC compound | SABIC Innovative Plastics Europe | PC | LNP™ THERMOCOMP™ |
| Sylvin 916VO Red 6256 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |