LNP™ THERMOCOMP™ MF008GS compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 67g8b7_LNP-THERMOCOMP-MF008GS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* MF008GS is a compound based on Polypropylene resin containing 40% Mixed Glass. Added features of this grade include: Chemically Coupled, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MFX-1008 HS MG Product reorder name: MF008GS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.87 | % | |
| Across Flow : 24 hr | 1.4 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 5780 | MPa | ASTM D638 |
| -- | 5300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 52.0 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2/5 |
| Break 3 | 51.0 | MPa | ASTM D638 |
| Break | 49.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.3 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 3.1 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4810 | MPa | ASTM D790 |
| -- 7 | 4680 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 84.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 87.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 58 | J/m | ASTM D256 |
| 23°C 9 | 5.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 10 | 23 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.6 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 157 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 153 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 130 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPSiV™ 4200-80A | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| Ferro PE RPE10HW14BK | Ferro Corporation | PE, Unspecified | Ferro PE |
| GPPC ABS D-120N | GPPC Chemical Co., Ltd. | ABS | GPPC ABS |
| Hax™ HF 4024 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| E-RIALFILL B 15 40 C | RIALTI Srl | PP, Unspecified | E-RIALFILL |