Celanex® 3201
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 66X6mI_Celanex3201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 3201 is a 15% glass reinforced general purpose thermoplastic polyester resin that offers a superior combination of mechanical, electrical, and thermal properties, together with outstanding processability, good chemical resistance, and toughness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.41 | g/cm³ | ASTM D792 |
| -- | 1.42 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Flow | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 93.1 | MPa | ASTM D638 |
| Fracture | 100 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 3.0 | % | ASTM D638 |
| Fracture | 3.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 5600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 213 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 218 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 192 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 195 | °C | ISO 75-2/A |
| Glass Transition Temperature | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 2 | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.50 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| -- | HB | UL 94 | |
| 0.9 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20 - 50 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65 - 93 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Feed Temperature: 230 to 240°CZone 4 Temperature: 240 to 260°CManifold Temperature: 250 to 260°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 52G1MX 25 GREY 7035 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| VENELENE® FB-7000 | Poliolefinas Internacionales, C.A. (Polinter) | LDPE | VENELENE® |
| Elexar® EL-86-K935F UV | Teknor Apex Company | TPE | Elexar® |
| Hifax TYC 356P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Karina IVORY TR (SP31503) -E TR-600N35/ 1-YT-A | Karina Ind. e Com. de Plásticos Ltda | TPE | Karina |