E-RIALFILL H 15 20 T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 662yPi_E-RIALFILL-H-15-20-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene compound, homopolymer obtained by total recycling of industrial scraps, 20% filled with talc. High flowability for injection molding, good dimensional stability and planarity Available just in black version. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.3 | % | |
| Flow | 1.3 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Ash Content | 20 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 28.0 | MPa | |
| Break, 23°C | 23.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 5.5 | % | |
| Break, 23°C | 25 | % | |
| Flexural Modulus 2(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 41.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 33 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 1.9 | kJ/m² | |
| 23°C | 2.3 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/A50 |
| -- | 92.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KEG-2001-50A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| NANCAR® 1072CG | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| ALCOM® PC 740/4 UV WT1445-06LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Colorite 66 Series 8066 | Colorite Polymers | PVC, Unspecified | Colorite 66 Series |
| LNP™ LUBRICOMP™ RX99518 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |