NORYL™ CN5260 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 660HhT_NORYL-CN5260-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% filled FR high modulus PPE/PS blend |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.15 to 0.25 | % | Internal Method |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 129 | MPa | Internal Method |
| Tensile Elongation (Break) | 5.0 | % | Internal Method |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 162 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 58 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 125 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 2.0E-5 to 3.1E-5 | cm/cm/°C | ASTM E831 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 10.2.0 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| Akulon® Diablo HT-HG6 (K-X07031) | DSM Engineering Plastics | Nylon 66/6 | Akulon® |
| Arak LLDPE HD5218EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| Latan 2 | LATI S.p.A. | Acetal (POM) Copolymer | Latan |
| LNP™ STAT-KON™ KD000 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |