CALP 3511G
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | CALP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 65xGN0_CALP-3511G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALP 3511G is a Polyolefin product. It can be processed by injection molding and is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 1.5 | % | |
| Across Flow : 2.00 mm | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 17 | % | ASTM D638 |
| Flexural Modulus | 2780 | MPa | ASTM D790 |
| Flexural Strength | 54.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 5.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 134 | °C | ASTM D648 |
| Ball Pressure Test (150°C) | Pass | Internal Method | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 80 | ASTM D2457 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEMICOSIL® 925 | Wacker Chemie AG | Silicone | SEMICOSIL® |
| ACCUTECH™ HP0339T40L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Dynaprene® SE9060A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Lupoy® GN5008HF | LG Chem Ltd. | PC+ABS | Lupoy® |
| Osterlene® LLDH-1-918 | Osterman & Company | LLDPE | Osterlene® |