Horda E8900
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Horda Cable Compounds |
| Trademark: | Horda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 65kl9q_Horda-E8900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Strippable Semiconductive Shielding E8900 is a crosslinkable, strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and for use in both dry and steam curing processes. E8900 meets the requirements as below, when optimal processing extrusion and end testing procedure are used: AEIC CS8 (latest edition) BS 6622 IEC 60502 NF C 33-223 NEMA WC 7-1996/ICEA S-95-658 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 - 1.18 | g/cm³ | ASTM D1928 |
| Mooney Viscosity (ML 1+4, 121°C) | 14 - 22 | MU | ISO 289 |
| Moisture Content 1 | ppm | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | IEC 60540 | ||
| 200°C 2 | % | IEC 60540 | |
| 200°C 3 | % | IEC 60540 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rheometer 4 | ISO 6502 | ||
| MH : 195°C | 0.200 - 0.341 | J | ISO 6502 |
| ML : 195°C | 0.0330 - 0.0550 | J | ISO 6502 |
| T90 : 195°C | 1.4 - 1.6 | min | ISO 6502 |
| Stripping Angle | 180 | ° | |
| Stripping Force 5 | |||
| EPR : 23°C | 2.3 - 2.5 | kN/m | |
| XLPE : 23°C | 1.3 - 1.7 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 - 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 250 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | -5.0 | % | ASTM D638 |
| Change in Ultimate Elongation in Air (135°C, 168 hr) | -50 | % | ASTM D638 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | < 5.0E+2 | ohms·cm | ASTM D257 |
| 90°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| 120°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 40.0 | °C | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Cylinder Zone 1 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 2 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 3 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 4 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 5 Temp. | 60.0 - 110 | °C | |
| Die Temperature | 100 - 130 | °C |
| Extrusion instructions |
|---|
| Neck Temperature: 100 to 130°CHead Temperature: 100 to 130°C |
| Note Message | |
|---|---|
| 1 . | QAHC-10420 (Karl Fischer method) |
| 2 . | 20 N/cm², PD |
| 3 . | 20 N/cm² |
| 4 . | Gottfert arc 0.2° |
| 5 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200-75A | RTP Company | TPU, Unspecified | RTP |
| REPOL® H033MG | Reliance Industries Limited | PP Homopolymer | REPOL® |
| UMG ALLOY® TC-80A | UMG ABS, Ltd. | PC+ABS | UMG ALLOY® |
| Lucky Enpla LAY3000 | Lucky Enpla Co LTD | PC+PBT | Lucky Enpla |
| Sylvin 6185-80 Grey 935 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |