RTP 900 P-1700
| Category: | PSU , Polysulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 65D1w1_RTP-900-P-1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL94 |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Moisture Content | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2480 | MPa | ASTM D638 |
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 75 | % | ASTM D638 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 2100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 181 | °C | |
| 1.8 MPa, Unannealed | 174 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 3.0E-3 | ASTM D150 | |
| Arc Resistance | 122 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 4.40 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 332 to 371 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Injection Pressure | 68.9 to 124 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Modified Plastics MN6-FG10 SE BK | Modified Plastics, Inc. | Nylon 6 | Modified Plastics |
| Clariant PBT PBT-1700G15 | Clariant Corporation | PBT | Clariant PBT |
| Hanwha Total PP FH44 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hanwha Total PP TF418 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Wanthane® WHT-8190RV | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | Wanthane® |