Nycal™ 2050R20
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Nycal™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 64wh2i_Nycal-2050R20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nycal™2050R20 is a polyamide 612 (nylon 6/12) material, and the filler is 20% glass fiber reinforced material. This product is available in North America and is processed by injection molding. Nycal™The main characteristics of 2050R20 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5860 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 193 | °C | ASTM D648 |
| Melting Temperature | 218 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Tensile Elongation, ASTM D638: 2 to 4%Volum Resistivity, ASTM D257: >1e13 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 - 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 - 304 | °C | |
| Mold Temperature | 65.6 - 98.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Compound 853 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| XANTAR® G4F 25 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| E-RIALFILL C HB 20 T | RIALTI Srl | PP Copolymer | E-RIALFILL |
| Pujie ACM-03 | Zhanhua Pujie Chemical Technology Co.,Ltd | CPE | Pujie |
| Sylvin 9077-95C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |