CYCOLAC™ FR15U resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 64v9Gz_CYCOLACFR15Uresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLAC FR15U is a flame retardant ABS with good processability and good indoor UV properties. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/5.0 kg) | 7.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.40 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2210 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 41.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 22 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2260 | MPa | ISO 178 |
| Flexural Stress | 63.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B50 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 20 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.80 mm | 5VA | UL 94 | |
| Oxygen Index | 26 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 195 - 225 | °C | |
| Front Temperature | 195 - 225 | °C | |
| Nozzle Temperature | 190 - 220 | °C | |
| Processing (Melt) Temp | 200 - 230 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1083 | RTP Company | PBT | RTP |
| Sylvin 916VO-90 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Geon™ Vinyl Rigid Extrusion 87564 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Huafon JF-D-8608 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Sylvin 8310-75C UV White 1507 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |