Estane® TS92AP7 NAT 021
| Category: | TPU-PC , Thermoplastic Polyurethane Elastomer (PC Based) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 64uOOA_EstaneTS92AP7NAT021.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® TS92AP7 NAT 021 is an aromatic polycarbonate-based thermoplastic polyurethane. Application: Extrusion |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 1 sec) | 93 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance | 39.0 | mm³ | ISO 4649-A |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 527-3/200 | ||
| Fracture | 60.0 | MPa | ISO 527-3/200 |
| 50% strain | 14.0 | MPa | ISO 527-3/200 |
| 100% strain | 18.0 | MPa | ISO 527-3/200 |
| 300% strain | 44.0 | MPa | ISO 527-3/200 |
| Tensile Elongation 2(Break) | 380 | % | ISO 527-3/200 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3 | 100 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 88.0 | °C | ISO 306/A50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 205 | °C | |
| Cylinder Zone 3 Temp. | 210 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Adapter Temperature | 210 | °C | |
| Die Temperature | 205 | °C |
| Extrusion instructions |
|---|
| Dew Point: -30°C to -40°CDie Tip: 200°C |
| Note Message | |
|---|---|
| 1 . | Type 5A |
| 2 . | Type 5A |
| 3 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AR36NT8506 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| ULTEM™ HU2210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| NEXT SIGNATURE PA6 GM40-300 | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT SIGNATURE |
| NuSil MED-6342 | NuSil Technology | Silicone | NuSil |
| Lucon® CP6067 | LG Chem Ltd. | PC | Lucon® |