Ultramid® T 4381 LDS
| Category: | Nylon 6/6T , Polyamide 6/6T Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 64dPhH_Ultramid-T-4381-LDS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass fibre and mineral reinforced partially aromatic polyamide for injection moulding. Good toughness, stiffness and strength, low water absorption, high melting point (295 °C). The product is especially tailored for laser direct structuring (LDS). The structured areas can be metallized selectively. The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG (Osteriede 7 - 30827 Garbsen - Germany). The use of this process asserts a claim for compensation. After purchasing a LPKF laser system the claim is satisfied. Please contact directly LPKF Laser & Electronics AG (http://www.LPKF.de). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.75 | -- | % | ISO 294-4 |
| Flow direction | 0.55 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.2 - 5.2 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.80 - 1.2 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8300 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 105 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 265 | -- | °C | ISO 75-2/B |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 5.0E-5 - 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 4.40 | 4.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 1.5E-3 | 0.038 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| Polymer Abbreviation | PA6T/6 GF10M25 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec | ||
| Drying Temperature | 110 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 300 | °C | |
| Middle Temperature | 310 | °C | |
| Front Temperature | 315 | °C | |
| Nozzle Temperature | 315 | °C | |
| Processing (Melt) Temp | 310 - 330 | °C | |
| Mold Temperature | 70.0 - 100 | °C |
| Injection instructions |
|---|
| Residence Time : <5 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® HP 3500 | Plastic Solutions, Inc. | PP Homopolymer | PrimaFlex® |
| Miramid® SE15C | BASF Leuna GmbH | Nylon 66 | Miramid® |
| Fluon® PFA P-62XPT | Asahi Glass Co., Ltd. | PFA | Fluon® |
| KOCETAL® K300 SB | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| ALTECH® PA66 ECO 1000/500 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |