NILAMID® A3 H CF20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 64Wc6z_NILAMID-A3-H-CF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NILAMID® A3 H CF20 is a Polyamide 66 (Nylon 66) compound, 20% carbon fiber reinforced, heat stabilized. This compound is intended for injection molding. NILAMID® A3 H CF20 is primarily designed for the Automotive industry. It is also suitable for Industrial & Consumer applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.50 | % | |
| Flow : 23°C | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.0 | % | |
| Saturation, 23°C | 6.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 15500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 200 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | 50 | kJ/m² | |
| 30°C | 40 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 258 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 130 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+3 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+4 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 2.4 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | < 100 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Oxygen Index | 28 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Duron PA 6,6 10GF-IML | ProPolymers Inc. | Nylon 66 | Duron |
| HyTemp® AR212HR | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |
| INELEC ABS SS10 | Infinity LTL Engineered Compounds | ABS | INELEC |
| Karina BLACK PVC COMPOUND 807D48/1-D-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LubriOne™ LB6600-5010 BK | PolyOne Corporation | Nylon 66 | LubriOne™ |