| Thermoplastic Polyester-Polyurethane with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping characteristic and high resilience performance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 62 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 390 | MPa | ISO 527-2 |
| Abrasion Loss | 30.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 17.0 | MPa | DIN 53504-S2 |
| 100% strain | 24.0 | MPa | DIN 53504-S2 |
| 300% strain | 35.0 | MPa | DIN 53504-S2 |
| Tensile Stress | DIN 53504-S2 | ||
| Yield | 50.0 | MPa | DIN 53504-S2 |
| Yield 1 | 43.0 | MPa | DIN 53504-S2 |
| Tensile Elongation | DIN 53504-S2 | ||
| Fracture | 400 | % | DIN 53504-S2 |
| Fracture 2 | 420 | % | DIN 53504-S2 |
| Tear Strength 3 | 200 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 40 | % | ISO 815 |
| 70°C, 24 hr | 55 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 210 - 220 | °C | |
| Middle Temperature | 215 - 230 | °C | |
| Front Temperature | 220 - 230 | °C | |
| Nozzle Temperature | 225 - 235 | °C | |
| Processing (Melt) Temp | 220 - 230 | °C | |
| Mold Temperature | 30 - 60 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Note Message | |
|---|---|
| 1 . | after storage in water for 21 days at 80°C |
| 2 . | after storage in water for 21 days at 80°C |
| 3 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PE XL8081UC | Sincerity Australia Pty Ltd. | PE, Unspecified | Sindustris PE |
| Sylvin 2927-67LG CLear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SureSpec HP-120NA | Genesis Polymers | PP Homopolymer | SureSpec |
| NYCOA Polyamide 2063 | Nycoa (Nylon Corporation of America) | Nylon 66/6 | NYCOA Polyamide |
| LNP™ THERMOCOMP™ LC008E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |