Pyramid™ II230
| Category: | PEI , Polyether Imide |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Pyramid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 629MTt_Pyramid-II230.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compression Molded Shape, Polyetherimide, Electro-Static Dissipative |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 1.4 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4100 | MPa | ASTM D638 |
| Tensile Strength | 75.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 3400 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (0.318 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | ESD S11.11 | ||
| -- 1 | 1.0E+8 to 1.0E+11 | ohms | |
| -- 2 | 1.0E+9 to 1.0E+12 | ohms | |
| Volume Resistivity | ESD S11.12 | ||
| -- 3 | 1.0E+8 to 1.0E+11 | ohms·cm | |
| -- 4 | 1.0E+9 to 1.0E+12 | ohms·cm | |
| Static Decay | 0.00200 | FTMS 101C 4046.1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 100 Volts |
| 2 . | 10 Volts |
| 3 . | 100 Volts |
| 4 . | 10 Volts |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 321S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Wondel® S SN0W | Nanjing Julong Engineering Plastics Co., LTD | ABS | Wondel® S |
| Ferro PP NPP00GD01BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| KOPA® KN135HB40BL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| ICORENE® 1314 | ICO Polymers EMEA, A Division of A. Schulman | LMDPE | ICORENE® |